Early age carbonation heat and products of tricalcium silicate paste subject to carbon dioxide curing

Abstract

This paper presents a study on the carbonation reaction heat and products of tricalcium silicate (C3S) paste exposed to carbon dioxide (CO2) for rapid curing. Reaction heat was measured using a retrofitted micro-calorimeter. The highest heat flow of a C3S paste subject to carbonation curing was 200 times higher than that by hydration, and the cumulative heat released by carbonation was three times higher. The compressive strength of a C3S paste carbonated for 2 h and 24 h was 27.5 MPa and 62.9 MPa, respectively. The 24-h carbonation strength had exceeded the hydration strength at 28 days. The CO2 uptake of a C3S paste carbonated for 2 h and 24 h was 17% and 26%, respectively. The X-ray diffraction (XRD), transmission electron microscope coupled with energy dispersive spectrometer (TEM-EDS), and 29Si magic angle spinning-nuclear magnetic resonance (29Si MAS-NMR) results showed that the products of a carbonated C3S paste were amorphous silica (SiO2) and calcite crystal. There was no trace of calcium silicate hydrate (C-S-H) or other polymorphs of calcium carbonate (CaCO3) detected.