Direct Observation via In Situ Heated Stage EBSD Analysis of Recrystallization of Phosphorous Deoxidised Copper in Unstrained and Strained Conditions

Abstract

Abstract: Recrystallization of phosphorous deoxidised copper used for strength critical applications at elevated temperatures was investigated by means of in situ heated stage EBSD analysis using a Gatan Murano heated stage mounted within a Carl Zeiss Sigma FEGSEM electron microscope. The influence of applied strain as the result of deformation within a Nakajima test as an analogue for industrial forming on the recrystallization temperature was investigated, the impact of increased heating rates on microstructural evolution was also investigated. Inverse pole figure plots combined with regions of reduction in local misorientations and variations in geometrically necessary dislocations were used to establish the point of recrystallization and the recrystallized fraction of the material. Recrystallization was observed to occur at temperatures as low as 130 °C in highly strained samples compared to around 300 °C within the annealed samples dependent upon heating rate. Increased heating rates were observed to produce a finer final grain structure but had little effect on presence of <111> 60° grain twins, which was influenced more by initial material condition. Graphic Abstract: [Figure not available: see fulltext.]