Structural, morphological and magnetic properties of hexaferrite BaCo2Fe16O27 nanoparticles and their efficient lead removal from water

Abstract

W-hexaferrite BaCo2Fe16O27 was prepared using the citrate nitrate combustion method. The sample was characterized using XRD, SEM, EDX and elemental mapping. XRD confirmed that the sample was synthesized in a single phase hexagonal structure with an average crystallite size 37.39 nm. SEM images of the sample show a spongy morphology with the agglomerated grain owing to dipole interaction between the crystallites. The magnetic properties of BaCo2Fe16O27 were studied using H-M hysteresis loop and the DC magnetic susceptibility. The sample has a ferrimagnetic behavior with saturation magnetization 64.133 emu/g. The magnetic properties of BaCo2Fe16O27 are originated from the Fe3+–O–Fe3+ superexchange. The synthesized sample is used as an adsorbent to remove the heavy metal Pb2+ from water. BaCo2Fe16O27 has Pb2+ removal efficiency 99% and 28% at pH 8 and 7 respectively. The Langmuir and Freundlich isotherms were used to analyze the experimental data. The Freundlich adsorption isotherm fitted the experimental data well.