Superplastic behaviour of AZ61-F magnesium composite materials

Abstract

Deformation of AZ61-F magnesium alloys with 1 wt?% of Al2O3 phase was tested at different temperatures and different strain rates. It was shown that at temperatures 473-523 K and the highest strain rate applied from 1×10-2 s-1 to 1×10-4 s-1, a significant ductility growth was observed. The grain size of 0.6-0.8 μm was reached by severe plastic deformations by means of equal channel angular pressing (ECAP). Secondary Mg17Al12 and Al2O3 phases were identified. Maximum strain was gained at temperature of 473 K and strain rate of 1×10-4 s-1.