Morphology and crystallography analyses of HSLA steels with hardenability enhanced by tailored C–Ni collocation

Abstract

High hardenability is of great importance to ultra-heavy steel plates and can be achieved by tailoring the composition of steel. In this study, the continuous cooling transformation (CCT) curves of two high-strength low-alloy (HSLA) steels (0.16C-0.92Ni steel and 0.12C-1.86Ni steel) were elucidated to reveal the significance of C–Ni collocation on hardenability from the perspective of morphology and crystallography. At a low cooling rate (0.5◦C/s), the 0.12C-1.86Ni steel showed higher microhardness than 0.16C-0.92Ni steel. The microstructure in 0.16C-0.92Ni steel was mainly granular bainite with block-shaped martensite/austenite islands (M/A islands), while that in 0.12C-1.86Ni steel was typically lath bainite with film-shaped M/A islands, denoting that the 0.12C-1.86Ni steel is of higher hardenability. Moreover, the 0.12C-1.86Ni steel exhibited a higher density of block boundaries, especially V1/V2 boundaries. The higher density of block boundaries resulted from the weakened variant selection due to the larger transformation driving force and more self-accommodation of transformation strain induced by the reduced carbon and increased nickel content.