Photocrosslinking of thin polymer films - Materials for sensors and actuators

Abstract

Polymers with temperature dependent degrees of swelling, especially polymers which exhibit lower critical solution temperature (LCST) behaviour in aqueous solutions, are of interest for applications in microsystems. For these applications it is necessary to form and pattern thin films in the μm-range. This has been achieved through photocrosslinking of linear prepolymers. Copolymers based on N-isopropylacrylamide (NIPAAm) were modified with a stilbazolium salt chromophore to yield photocrosslinkable temperature sensitive polymers. The chromophore reacts via a [2+2]-cycloaddition under irradiation, this can be used to crosslink the polymer. The photocrosslinking properties were studied by UV irradiation of thin films and measuring the changes in UV absorption spectra. Through irradiation of thin films through a mask it was possible to obtain patterned networks in the μm-range (20 μm space width and > 50 μm line width). The polymers exhibited LCST behaviour, which was measured using DSC. The resulting patterned networks had temperature dependent swelling properties in aqueous media.