Translucent thin film Fe2O3 photoanodes for efficient water splitting by sunlight: Nanostructure-directing effect of Si-doping

Abstract

Thin, silicon-doped nanocrystalline α-Fe2O3 films have been deposited on F-doped SnO2 substrates by ultrasonic spray pyrolysis and chemical vapor deposition at atmospheric pressure. The photocatalytic activity of these films with regard to photoelectrochemical water oxidation was measured at pH 13.6 under simulated AM 1.5 global sunlight. The photoanodes prepared by USP and APCVD gave 1.17 and 1.45 mA/cm2, respectively, at 1.23 V vs RHE. The morphology of the α-Fe2O3 was strongly influenced by the silicon doping, decreasing the feature size of the mesoscopic film. The silicon-doped α-Fe2O3 nano-leaflets show a preferred orientation with the (001) basal plane normal to the substrate. The best performing photoanode would yield a solar-to-chemical conversion efficiency of 2.1% in a tandem device using two dye-sensitized solar cells in series. Copyright © 2006 American Chemical Society.