Mechanical Performance of Portland Cement, Coarse Silica Fume, and Limestone (PC-SF-LS) Ternary Portland Cements

Abstract

Ternary Portland cements composed of coarse silica fume (SF), limestone (LS), and Portland cement (PC) can afford some environmental advantages by reducing the clinker content in Portland cements. These cements will help to reduce the clinker factor target from 0.78 to 0.60 by 2050 with the aim to be climate neutral. Silica fume (SF) possesses pozzolanic properties that enhance mechanical strength and durability. By contrast, limestone powder has three main outcomes, i.e., filler, dilution, and chemical effects. The first reduces porosity and refines the microstructure of mortars and concretes. The second decreases the amount of hydration products and increases the porosity; the third one promotes the appearance of carboaluminates and reduces porosity. This paper covers the mechanical properties of Portland cement-limestone-coarse silica fume ternary cements, and its synergetic mechanism. Compressive and flexural strength of mortar at 2, 7, 14 and 28 days was performed. Coarse silica fume has a minor contribution on the nucleation effect compared to ground limestone at early ages. The nucleation and filler effects, at early ages, are less pronounced in coarse and very fine limestone powder. The highest compressive strength at 28 days is reached with the lowest content of coarse silica fume (3%). Mortar mixes made with a high level of limestone presented a delay in the compressive strength development.