Data-Driven Prediction of Tensile Strength and Hardness in Ultrasonic Vibration-Assisted Friction Stir Welding of AA6082-T6

Abstract

This work investigates how ultrasonic vibration can enhance friction stir welding (FSW) of an AA6082-T6 aluminium alloy and develops a data-driven tool to predict joint performance from process settings. A custom ultrasonic transducer and horn were designed and tuned using finite element modal and harmonic analyses, confirming a strong longitudinal resonance near 27.9 kHz with a tip amplitude of about 46 µm. A 27-run factorial experiment varied tool rotation (600–900 rpm), welding speed (45–55 mm/min), and plunge depth (0.10–0.25 mm). Welded joints were assessed using tensile strength and Vickers hardness. Four predictive models, support vector regression (SVR), Gaussian process regression (GPR), artificial neural networks (ANNs), and multiple linear regression (MLR) were trained and compared under five-fold cross-validation. The best joint quality was obtained at 900 rpm, 55 mm/min, and a 0.25 mm plunge depth, yielding a tensile strength of 188.7 MPa and a hardness of 102 HV. Overall, MLR provided the strongest predictive performance while remaining interpretable (UTS R2 = 0.81, RMSE = 11.84 MPa; hardness R2 = 0.67, RMSE = 2.36 HV), matching the ANN for UTS prediction and outperforming the ANN, GPR, and SVR for hardness. A coupling physics-based ultrasonic design with an interpretable predictive model offers a practical route to reduce trial and error, improve parameter selection, and accelerate the process development for ultrasonic vibration-assisted FSW of aluminium alloys; however, modest models can outperform complex ones when the dataset is limited.