Analysis of Internal Defects Appeared in the Continuous Casting

Abstract

The paper presents the study of internal defects resulting from the continuous casting of steels. The 50 samples were taken from a total of 20 continuously cast bits of different steel grades. The investigation of the causes of internal defects, shown on the analyzed samples, started from the assumption that the secondary metallurgy was performed correctly. The following internal defects have been evident: internal cracks (axial cracks, section cracks), central porosity and marginal punctuation impurities.