Surface Chemical Effects on Fischer–Tropsch Iron Oxide Catalysts Caused by Alkali Ion (Li, Na, K, Cs) Doping

Abstract

Among the alkali metals, potassium is known to significantly shift selectivity toward value-added, heavier alkanes and olefins in iron-based Fischer–Tropsch synthesis catalysts. The aim of the present contribution is to shed light on the mechanism of action of alkaline promoters through a systematic study of the structure–reactivity relationships of a series of Fe oxide FTS catalysts promoted with Group I (Li, Na, K, Cs) alkali elements. Reactivity data are compared to structural data based on in situ, synchrotron-based XRD and XPS, as well as temperature-programmed studies (TPR-H2, TPC-CO, TPD-CO2, and TPD-H). It has been observed that the alkali elements induced higher carburization rates, higher basicities, and lower adsorbed hydrogen coverages. Catalyst stability followed the trend Na-Fe > unpromoted > Li-Fe > K-Fe > Cs-Fe, being consistent with the ability of the alkali (Na) to prevent active site loss by catalyst reoxidation. Potassium was the most active in promoting high α hydrocarbon formation. It is active enough to promote CO dissociative adsorption (and the formation of FeCx active phases) and decrease the surface coverage of H-adsorbed species, but it is not so active as to cause premature catalyst deactivation by the formation of a carbon layer resulting in the blocking active sites.