Production of palm frond based wood plastic composite by using twin screw extruder

Abstract

Wood plastic composite (WPC) is the blending product from wood as filler and polymer thermoplastic as matric. Palm frond waste is a material with selulose about 68%, so it has potential to be developed as raw material for WPC. The purpose of this research was to learn how to produce WPC based on palm frond use twin screw extruder. It used popropilen as matric. As for aditif, it used Maleated Polypropilene (MAPP) as compatibilizer and paraffin as plasticizer. The size of palm frond is 40 - 80 mesh. WPC is made from blending polipropylene, palm frond, MAPP and paraffin with dry mixing method in room temperature. Then, PP, Palm frond and additive from dry mixing is fed into twin screw extruder at 190°C and 60 rpm. It use palm frond/polypropylene 60/40, MAPP 5% w/w and paraffin 2% w/w. From the result, it shown that WPC based on palm frond met the standards forcommercial WPC. It has tensile strength up to 19.2 MPa, bending strength 43.6 MPa and water adsorption 0,32% w/w. So, WPC based on palm frond has prospective to be developed for commercial WPC.