The impact of P(NDI2OD-T2) crystalline domains on the open-circuit voltage of bilayer all-polymer solar cells with an inverted configuration

Abstract

We fabricated P(NDI2OD-T2)/PTB7 bilayer all-polymer solar cells with an inverted configuration, where the annealing temperature was systematically varied. The current density-voltage behavior was investigated and the structural properties of the P(NDI2OD-T2) layers were characterized. Absorption spectroscopy, surface morphology, and crystallite analysis showed that increasing phase segregation of P(NDI2OD-T2) films occurred as the annealing temperature increased. We found that, as the P(NDI2OD-T2) stacking improved, with larger domains, the open-circuit voltage decreased and the saturation dark current density increased. This work provides a guide for the processing of P(NDI2OD-T2) layers to maximize the power conversion efficiency of all-polymer solar cells.