High- κ Al2O3 material in low temperature wafer-level bonding for 3D integration application

Abstract

This work systematically investigated a high-κ Al2O 3 material for low temperature wafer-level bonding for potential applications in 3D microsystems. A clean Si wafer with an Al2O 3 layer thickness of 50 nm was applied as our experimental approach. Bonding was initiated in a clean room ambient after surface activation, followed by annealing under inert ambient conditions at 300 C for 3 h. The investigation consisted of three parts: a mechanical support study using the four-point bending method, hermeticity measurements using the helium bomb test, and thermal conductivity analysis for potential heterogeneous bonding. Compared with samples bonded using a conventional oxide bonding material (SiO2), a higher interfacial adhesion energy (∼11.93 J/m2) and a lower helium leak rate (∼6.84 × 10-10 atm.cm3/sec) were detected for samples bonded using Al2O3. More importantly, due to the excellent thermal conductivity performance of Al 2O3, this technology can be used in heterogeneous direct bonding, which has potential applications for enhancing the performance of Si photonic integrated devices. © 2014 Author(s).