Abstract
In this paper, high-nitrogen steel (HNS) was joined by vacuum brazing using an Ag-Cu-Ni filler metal and the effect of brazing temperature and duration time on the evolution of mechanical properties and microstructure of HNS joints were analyzed. The results showed that the optimal brazing temperature was 950°C and the optimal shear strength was obtained with the value of 212.4 MPa when the brazing temperature was 950°C with the brazing time of 10 min.
Author supplied keywords
Cite
CITATION STYLE
Wang, X., Li, Z., Gao, D., Li, S., Peng, J., Zhang, S., … Long, W. (2022). Microstructure and joint properties of high-nitrogen steel brazed by AgCuNi filler metal. International Journal of Modern Physics B, 36(5). https://doi.org/10.1142/S021797922250045X