Synthesis and characterisation of dyeintercalated nickel-aluminium layereddouble hydroxide as a cosmetic pigment

Abstract

Dye-intercalated layered double hydroxides (LDH) are modern promising pigments for paint and cosmetics industry. For the preparation of high-quality cosmetic pigments, particularly for nail polish, it was proposed to use not only intercalation but also chemisorption. For the pigment synthesis, Ni-AL LDH was chosen, along with murexide (Ammonium (purpurate) 2,6-dioxo-5-[(2,4,6-trioxo-5-hexahydropyrimidinylidene)amino]-3H-pyrimidin-4-olate), in which colored purpurate anion is able to form complex compounds with Ni2+. The murexide-intercalated (murexide amount for intercalation only) and murexide-intercalated-chemisorbed (murexide amount for Ni2+) Ni-Al LDH pigments were synthesized and used for the preparation of nail polish samples. The crystallographic composition was studied by means of XRD analysis. The color parameters (coordinates of color and chromaticity, dominant wavelength and color purity) of pigment powders and nail polish samples with these pigments have been studied using a color comparator. Organoleptic characteristics of pigment and nail polish samples were studied. The positive influence of chemisorption was shown: murexide-intercalated-chemisorbed pigment is easily ground, with the formation of highly dispersed powder, which during the preparation of nail polish was easily dispersed with the formation of stable yellow samples (dominant wavelength 583 nm) with high color purity of 43 %. Also, high covering ability of the murexide-intercalated-chemisorbed pigment was shown: high-quality, opaque, colored nail polish coat was formed at the pigment content of 45 %, 30 % and 15 % (wt.). For the synthesis of such pigments, it was recommended to choose anionic dyes that can form coordination bonds with LDH cations.