Carbon microsphere-supported metallic nickel nanoparticles as novel heterogeneous catalysts and their application for the reduction of nitrophenol

Abstract

Nickel nanoparticles are gaining increasing attention in catalysis due to their versatile catalytic action. A novel, low-cost and facile method was developed in this work to synthesize carbon microsphere-supported metallic nickel nanoparticles (Ni-NP/C) for heterogeneous catalysis. The synthesis was based on carbonizing a polystyrene-based cation exchange resin loaded with nickel ions at temperatures between 500 and 1000◦C. The decomposition of the nickel-organic framework resulted in both Ni-NP and carbon microsphere formation. The phase composition, morphology and surface area of these Ni-NP/C microspheres were characterized by powder X-ray diffraction, Raman spectroscopy, scanning electron microscopy and BET analysis. Elemental nickel was found to be the only metal containing phase; fcc-Ni coexisted with hcp-Ni at carbonization temperatures between 500 and 700◦C, and fcc-Ni was the only metallic phase at 800–1000◦C. Graphitization and carbon nanotube formation were observed at high temperatures. The catalytic activity of Ni-NP/C was tested in the reduction of 4-nitrophenol to 4-aminophenol by sodium borohydride, and Ni-NP/C was proved to be an efficient catalyst in this reaction. The relatively easy and scalable synthetic method, as well as the easy separation and catalytic activity of Ni-NP/C, provide a viable alternative to existing nickel nanocatalysts in future applications.