Electrode Kinetics of the Ni Porous Electrode for Hydrogen Production in a Molten Carbonate Electrolysis Cell (MCEC)

Abstract

© 2015 The Electrochemical Society. All rights reserved.The purpose of this study was to elucidate the kinetics of a porous nickel electrode for hydrogen production in a molten carbonate electrolysis cell. Stationary polarization data for the Ni electrode were recorded under varying gas compositions and temperatures. The slopes of these iR-corrected polarization curves were analyzed at low overpotential, under the assumption that the porous electrode was under kinetic control with mass-transfer limitations thus neglected. The exchange current densities were calculated numerically by using a simplified porous electrode model.Within the temperature range of 600-650°C, the reaction order of hydrogen is not constant; the value was found to be 0.49-0.44 at lower H 2 concentration, while increasing to 0.79-0.94 when containing 25-50% H 2. The dependence on CO 2 partial pressure increased from 0.62 to 0.86 with temperature. The reaction order of water showed two cases as did hydrogen. For lower H 2 O content (10-30%), the value was in the range of 0.47-0.67 at 600-650°C, while increasing to 0.83-1.07 with 30-50% H 2 O. The experimentally obtained partial pressure dependencies were high, and therefore not in agreement with any of the mechanisms suggested for hydrogen production in molten carbonate salts in this study.