Microstructure and properties of TiAIN/a-C nanocomposite coatings prepared by reactive sputtering

13Citations
Citations of this article
16Readers
Mendeley users who have this article in their library.

Abstract

TiAIN/a-C nano-composite coatings were synthesized by a reactive co-sputtering process to investigate the effects of sputtering conditions on the microstructure and mechanical properties. Coating films were deposited on square plates of Si and high speed steel (ANSI M2) by the cosputtering of TiAl (pulsed-d.c. sputtering) and C (d.c. sputtering) targets using a "Facing Target-type Sputtering" system at an atmosphere with a mixture of Ar and N2 but without hydrocarbon gas. The structure of the coatings was investigated by means of XRD, XPS and HRTEM with GIF (Gatan Imaging Filter). Mechanical properties of coating films were measured by a submicron indentation system. Though TiAIN and a-C coatings showed hardness of about 32 and about 10 GPa, respectively, TiAIN/a-C coatings containing 4.6 at% of C showed higher hardness of 43GPa. The energy filter images depicted that a change of contrast in the zero-loss image corresponded to nanometer-size of Ti agglomerates in Ti map. Cls spectrum in XPS analysis revealed that carbon in the coatings was bounded as C-C and C-N without bonding of Ti-C or Al-C. These results indicated that the TiAIN/a-C nano-composite coatings consisted of complicated mixture of nanocrystalline li-Al-N phase and a-C phase (including C-N bonding). © 2010 The Japan Institute of Metals.

Cite

CITATION STYLE

APA

Nose, M., Kawabata, T., Khamseh, S., Matsuda, K., Fujii, K., Ikeno, S., & Chiou, W. A. (2010). Microstructure and properties of TiAIN/a-C nanocomposite coatings prepared by reactive sputtering. Materials Transactions, 51(2), 282–287. https://doi.org/10.2320/matertrans.MC200913

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free