Study of thin film poly-crystalline CdTe solar cells presenting high acceptor concentrations achieved by in-situ arsenic doping

13Citations
Citations of this article
27Readers
Mendeley users who have this article in their library.

Abstract

Doping of CdTe using Group-V elements (As, P, and Sb) has gained interest in pursuit of increasing the cell voltage of CdTe thin film solar devices. Studies on bulk CdTe crystals have shown that much higher acceptor concentration than the traditional copper treatment is possible with As, P or Sb, enabled by high process temperature and/or rapid thermal quenching under Cd overpressure. We report a comprehensive study on in-situ As doping of poly-crystalline CdTe solar cells by MOCVD, whereby high acceptor densities, approaching 3 × 10 16 cm −3 were achieved at low growth temperature of 390 °C. No As segregation could be detected at grain boundaries, even for 10 19 As cm −3 . A shallow acceptor level (+0.1 eV) due to As Te substitutional doping and deep-level defects were observed at elevated As concentrations. Devices with variable As doping were analysed. Narrowing of the depletion layer, enhancement of bulk recombination, and reduction in device current and red response, albeit a small near infrared gain due to optical gap reduction, were observed at high concentrations. Device modelling indicated that the properties of the n-type window layer and associated interfacial recombination velocity are highly critical when the absorber doping is relatively high, demonstrating a route for obtaining high cell voltage.

Cite

CITATION STYLE

APA

Kartopu, G., Oklobia, O., Turkay, D., Diercks, D. R., Gorman, B. P., Barrioz, V., … Irvine, S. J. C. (2019). Study of thin film poly-crystalline CdTe solar cells presenting high acceptor concentrations achieved by in-situ arsenic doping. Solar Energy Materials and Solar Cells, 194, 259–267. https://doi.org/10.1016/j.solmat.2019.02.025

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free