High temperature sensing and detection for cementitious materials using manganese violet pigment

Abstract

In recent years, advanced materials have attracted considerable interest in the field of temperature detection and sensing. This study examined the thermochromic properties of inorganic manganese violet (MV) with increasing temperature. According to the thermochromic test, the material was found to have reversible and irreversible color change properties. The MV pigment was then applied to cementitious material at ratios of 1%, 3%, and 5%. The mixed cement samples with MV pigment were heated in a furnace, and digital images were captured at each temperature interval to evaluate the changes in the color information on the surface of the specimen. The mixed samples exhibited an irreversible thermochromic change from dark violet to grayish green above 400°C. At the critical temperature of 440°C, the RGB values increased by approximately 22%-55%, 28%-68%, and 7%-25%, depending on the content of MV pigment. In Lab space, the L value increased by approximately 23%-60% at 440°C. The a value completely changed from positive to negative, and the b value changed from negative to positive. All the values differed according to the content of MV pigment at room temperature but approached similar ranges at the critical temperature, irrespective of the amount of MV pigment. To assess the changes in their microstructure and composition, scanning electron microscopy and energy dispersive X-ray spectroscopy were performed on the samples exposed to temperatures ranging from room temperature to 450°C.