Enhanced Electrocatalytic Activity for ORR Based on Synergistic Effect of Hierarchical Porosity and Co-Nx Sites in ZIF-Derived Heteroatom-Doped Carbon Materials

Abstract

The hierarchical porosity and active sites of porous carbon materials have significant impacts on the oxygen reduction reaction (ORR) process. The heteroatom-doped porous carbon materials (Z67-900, Z8-900, Z11-900, Z12-900) were synthesized by pyrolysis of ZIFs to reveal the synergistic effect of hierarchical porosity and Co-Nx sites. The structures of prepared materials were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectra, and nitrogen adsorption. The results of electrocatalytic performance show that Z67-900 has the best performance among the four materials prepared. The onset potential (E0) of Z67-900 is close to commercial Pt/C (20%), and the half-wave potential (E1/2) of Z67-900 is 80 mV positive than that of Pt/C in an O2-saturated 0.1 M KOH solution (1600 rpm) with sweep rate of 5 mV·s−1. Moreover, Z67-900 has better methanol resistance. The hierarchical pore structure of Z67-900 facilitates mass transfer, while the Co-Nx sites provide active catalytic centers. This study provides a solid foundation for the rational design of highly efficient ZIF-derived heteroatom-doped catalysts.