Water-based Synthesis and Properties of a Scandium 1,4-Naphthalenedicarboxylate

Abstract

A new scandium naphthalenedicarboxylate with the framework composition [Sc2(1,4-NDC)3] (H2-1,4-NDC = 1,4-naphthalenedicarboxylic acid) was obtained under hydrothermal synthesis conditions. A structure model could be developed by a combination of 3D electron diffraction measurements and computationally assisted structure determination, which was further validated by a good agreement with the experimental powder X-ray diffraction pattern. The structure consists of isolated ScO6 octahedra interconnected by the carboxylate groups of linker molecules to form chains. These chains are connected by the naphthalene-moieties to form a three-dimensional framework with square-shaped pores and the organic group pointing into the pores. Although very similar synthesis conditions were chosen, [Sc2(1,4-NDC)3] is not isostructural to aluminum naphthalenedicarboxylate [Al(OH)(1,4-NDC)], which crystallizes in a MIL-53 type structure. This can be traced back to the different inorganic building units that are observed. The compound was thoroughly characterized by elemental analysis, IR spectroscopy, sorption measurements, thermogravimetric analysis and luminescence measurements. [Sc2(1,4-NDC)3] exhibits a high thermal stability and a ligand-based blue luminescence in the solid state at room temperature.