Influence of SiC Doping on the Mechanical, Electrical, and Optical Properties of 3D-Printed PLA

Abstract

Additive manufacturing, also known as 3D printing or digital fabrication technology, is emerging as a fast-expanding technology for the fabrication of prototypes and products in a variety of applications. This is mainly due to the advantages of 3D printing including the ease of manufacturing, the use of reduced material quantities minimizing material waste, low-cost mass production as well as energy efficiency. Polylactic acid (PLA) is a natural thermoplastic polyester that is produced from renewable resources and is routinely used to produce 3D-printed structures. One important feature that makes PLA appealing is that its properties can be modulated by the inclusion of nano or microfillers. This is of special importance for 3D-printed triboelectric nanogenerators since it can enhance the performance of the devices. In this work we investigate the influence of SiC micron-sized particles on the mechanical, electrical, and optical properties of a PLA-SiC composite for potential application in triboelectric energy harvesting. Our result show that the ultimate tensile strength of the pure PLA and 1%-doped PLA decreases with the number of fatigue cycles but increases by about 10% when SiC doping increases to 2% and 3%, while the strain at max load was about 3% independent of doping and the effective hardness was increased reaching a plateau at about 2 wt% SiC, about 40% above the value for pure PLA. Our results show that the mechanical properties of PLA can be enhanced by the inclusion of SiC, depending on the concentration of SiC. In addition, the same behavior is observed for the dielectric constant of the composite material increases as the SiC concentration increases, while the optical properties of the resulting composite are strongly dependent on the concentration of SiC.