Statistical Optimization of the Sol–Gel Electrospinning Process Conditions for Preparation of Polyamide 6/66 Nanofiber Bundles

Abstract

Polymeric nanofibers are widely studied in the textile industry since with them, it is possible to get a great variety of functionalities. In this paper, polyamide 6/66 (PA 6/66) solutions at different concentrations (12, 17, and 22% wt.) were made, to get nanofibers through the basic electrospinning process which were characterized by scanning electron microscope (SEM) and productivity. Afterwards, nanofiber bundles were produced using the electrospinning sol–gel process, which were characterized by SEM and tensile test. From the results of statistical optimization based on one-way analysis of variance (ANOVA) with post hoc Tukey HSD, it was found that nanofiber bundles with higher productivity (1.39 ± 0.15 mg/min), draw ratio (9.0 ± 1.2), and tensile strength (29.64 ± 7.40 MPa) were obtained with a 17% concentration. Finally, a thermal characterization through differential scanning calorimetry (DSC) was done, finding evidence of a Tg and Tm reduction in the nanofibers in relation to PA 6/66 pellets and nanofiber bundles.