Transport properties of transition-metal doped BiS2-based superconductors

Abstract

We performed the electrical resistivity and thermoelectric power measurements of the polycrystalline La0.8Ti0.2OBi(S1-xSex)2. The electrical resistivity of La0.8Ti0.2OBi(S0.7Se0.3)2 at room temperature dramatically decreases, and the temperature dependence shows metallic-like behavior. From the electrical resistivity, superconductivity was not observed in La0.8Ti0.2OBi(S1-xSex)2 above 2.8 K. The value of thermoelectric power S(300 K) of La0.8Ti0.2OBiSSe was about -65 μV/K, which is comparable to that of the polycrystalline LaOBiS2. The value of S(300 K) of La0.8Ti0.2OBiS2 was about -115 μV/K. These power factors are relatively smaller than that of the polycrystalline LaOBiSSe.