Solvent retention in thin polymer films studied by gas chromatography

Abstract

Thin polystyrene films were produced by spin coating from solutions in toluene. The amount of solvent retained in the films after drying for different times was measured using gas chromatography. Whereas for thicker films (thickness > 200 nm), the relative amount of solvent in the films is less than a few percent, the proportion of toluene increases significantly in thinner films. The thickness dependence of the mass of retained solvent shows that the solvent is mainly retained at the polymer-substrate interface. The solvent desorption rate exhibits no variation on the film thickness. © Springer-Verlag 2007.