Hot Corrosion Mechanism in Multi-Layer Suspension Plasma Sprayed Gd2Zr2O7 /YSZ Thermal Barrier Coatings in the Presence of V2O5 + Na2SO4

Abstract

This study investigates the corrosion resistance of two-layer Gd2Zr2O7/YSZ, three-layer dense Gd2Zr2O7/ Gd2Zr2O7/YSZ, and a reference single-layer YSZ coating with a similar overall top coat thickness of 300-320 µm. All the coatings were manufactured by suspension plasma spraying resulting in a columnar structure except for the dense layer. Corrosion tests were conducted at 900 °C for 8 h using V2O5 and Na2SO4 as corrosive salts at a concentration of approximately 4 mg/cm2. SEM investigations after the corrosion tests show that Gd2Zr2O7-based coatings exhibited lower reactivity with the corrosive salts and the formation of gadolinium vanadate (GdVO4), accompanied by the phase transformation of zirconia was observed. It is believed that the GdVO4 formation between the columns reduced the strain tolerance of the coating and also due to the fact that Gd2Zr2O7 has a lower fracture toughness value made it more susceptible to corrosion-induced damage. Furthermore, the presence of a relatively dense layer of Gd2Zr2O7 on the top did not improve in reducing the corrosion-induced damage. For the reference YSZ coating, the observed corrosion-induced damage was lower probably due to combination of more limited salt penetration, the SPS microstructure and superior fracture toughness of YSZ.