Effects of Tube Processing on the Fatigue Life of Nitinol

Abstract

Nitinol tubes were manufactured from Standard Grade VIM-VAR ingots using Tube Manufacturing method “TM-1.” Diamond-shaped samples were laser cut, shape set, then fatigued at 37 °C to 107 cycles. The 50, 5, and 1% probabilities of fracture were calculated as a function of number of cycles to fracture and compared with probabilities determined for fatigue data published by Robertson et al. (J Mech Behav Biomater 51:119–131, 2015). Robertson tested similar diamonds made from the same standard grade of Nitinol as in the current study, two other standard grades of Nitinol, and two high-purity grades of Nitinol expressly designed to improve fatigue life. Robertson’s tubes were manufactured using Tube Manufacturing method “TM-2.” Fatigue performance of TM-1 and TM-2 diamonds were compared: At 107 cycles, strain amplitudes corresponding to the three probabilities of fracture of the TM-1 diamonds were 2–3 times those of the TM-2 diamonds made from the same grade of Nitinol, and comparable to TM-2 diamonds made from the higher-purity materials. This difference is likely a result of the differences in tube manufacturing techniques and effects on resulting microstructures. Microstructural analyses of samples revealed a correlation between the median probability of fracture and median inclusion diameter that follows an inverse power-law function of the form y ≈ x−1.