The effect of aggregate aspect ratio and temperature on the fracture toughness of a low cement refractory concrete

Abstract

This work investigated the influence of the aggregate's aspect ratio on the fracture behavior of a low cement aluminum silicate refractory castable treated at two different temperatures (110 °C and 1000 °C). The aggregates were cylindrical pellets with an aspect ratio of 1, 2, 3 and 4, pro-duced by extruding a mixture of clay and calcined alumina fired at 1600 °C for 4 h to yield mullite (3Al 2 O 3 .2SiO 2). The behavior of the R-Curve and other relevant fracture parameters were evalu-ated based on the " Two Parameter Fracture Model " in a three-point flexure test of single-edge straight through notched specimens. The two temperature treatments produced different degrees of matrix-aggregate adhesion. The larger aspect ratio aggregates were found to promote toughen-ing only in the dried condition, at 110 °C, while the specimens fired at 1000 °C for 4 h, regardless of their aggregate aspect ratio, displayed no significant toughening. The best results for fired samples, however, were obtained from specimens containing conventional angular aggregates.