Epoxy Resin Nanocomposites: The Influence of Interface Modification on the Dispersion Structure—A Small-Angle-X-ray-Scattering Study

Abstract

The surface functionalization of inorganic nanoparticles is an important tool for the production of homogeneous nanocomposites. The chemical adaptation of the nano-filler surface can lead to effective weak to strong interactions between the fillers and the organic matrix. Here we present a detailed systematic study of different surface-functionalized particles in combination with a SAXS method for the systematic investigation of the interface interaction in the development of epoxy nanocomposites. We investigated the effect of surface modification of spherical SiO2 nanoparticles with 9 nm and 72 nm diameter and crystalline ZrO2 nanoparticles with 22 nm diameter on the homogeneous distribution of the fillers in diethylenetriamine (DETA) cured bisphenol-F-diglycidylether epoxy resin nanocomposites. Unmodified nanoparticles were compared with surface-modified oxides having diethylene glycol monomethyl ethers (DEG), 1,2-diols, or epoxy groups attached to the surface. The influence of surface modification on dispersion quality was investigated by transmission electron microscopy (TEM) and small angle X-ray scattering (SAXS) for inorganic filler contents of 3, 5 and 10 wt%. It was shown that the dispersion quality can be optimized by varying the coupling agent end group to obtain homogeneous and transparent nanomaterials. UV/VIS measurements confirmed the transparency/translucency of the obtained materials. The relationship between particle–matrix interaction and particle–particle interaction plays a decisive role in homogeneity and is controlled by the surface groups as well as by the type, size, and morphology of the nanoparticles themselves.