Coconut-Fiber Composite Concrete: Assessment of Mechanical Performance and Environmental Benefits

Abstract

The purpose of this qualification work is to study the physical and mechanical behavior of concrete with the addition of 0.5% and 1% coconut fiber, which has been subjected to two chemical treatments to reduce its degradation. The coconut fibers were extracted from the raw material and cut into pieces 4 cm long. Subsequently, the fibers were subjected to two chemical treatments. The first involved immersing the fibers in 4% sodium hydroxide (NaOH) solution, and the second treatment involved coating them with gum arabic and silica fume. A total of 50 samples of fibers were collected in their natural and post-treated state to be tested. The dosage was prepared for design strengths of 210 and 240 kg/cm2 (20.59 and 23.54 MPa), so that the percentages of 0.5% and 1% volume of coconut fiber, for the two treatments selected, replaced the respective volume of coarse aggregates. The cylinders with 1% addition of fibers had the best performance for the design strength of 20.59 MPa, including the cylinders without fibers. Those with 0.5% addition of fibers presented better performance for the 23.54 MPa dosage, although this was lower than the cylinders without fibers. In all cases, the cylinders with NaOH-treated fibers outperformed their counterparts with fibers treated with gum arabic and silica fume. Finally, a CO2 balance was determined, and an environmental gain up to 14 kg in CO2 emissions was established for each cubic meter of composite concrete.